|Size:||2-3mm, 3-5mm, 4-6mm||Water Content:||≤1.0|
|Color:||Beige||Package Moisture Content%≤:||1.5|
zeolite 3a molecular sieve,
molecular sieve type 3a,
beige zeolite 3a molecular sieve
3a Molecular Sieve Desiccant For CO2 And H2S Removal From Biogas Gas
Xi'an Lvneng Molecular Sieve type 3A is an alkali metal alumino-silicate; it is the potassium form of the type A crystal structure. Type 3A has an effective pore opening of about 3 angstroms (0.3nm). This is large enough to allow in moisture but excludes molecules such as unsaturated hydrocarbons which can potentially form polymers, and this maximizes lifetime when dehydrating such molecules.
|Molecular Sieve 3A Typical Physical Properties|
|Item||Unit||8*12 Mesh||4*6 Mesh|
|Bulk Density||g/ml ≥||0.70-0.82||0.65-0.80|
|Equilibrium Water Capacity @ 25℃||wt% ≥||19.0-21.0||19.0-21.0|
|Equilibrium Ethylene Capacity||mg/g≤||3.0||3.0|
|Heat of Adsorption||BTU/lb of H2O||1800||1800|
|Crush Strength||Point Contact||N ≥||20-58||80-130|
|Attrition Rate||wt% ≤||0.1||0.1|
|Size Qualification||% ≥||98||98|
|Package Moisture||wt% ≤||1.5||1.5|
|The interval value of the indexes above are on the basis of the different grade of Molecular Sieve 3A|
a) Drying of unsaturated hydrocarbons (e.g. ethylene, propylene, butadien)
b) Cracked Gas Drying
c) Drying of natural gas, if COS minimization is essential, or a minimum co-adsorption of hydrocarbons is required.
d) Drying of highly polar compounds, such as methanol and ethanol
e) Drying of liquid alcohol
f) Static, (non-regenerative) dehydration of insulating glass units, whether air filled or gas-filled.
g) Drying of CNG.
Xi'an Lvneng molecular sieve Type 3A can be regenerated by either heating in the case of thermal swing processes; or by lowering the pressure in the case of pressure swing processes.
To remove moisture from a 3A molecular sieve, a temperature of 200-230°C is required. A properly regenerated molecular sieve can give moisture dew points below -100°C.
The outlet concentrations on a pressure swing process will depend on the gas present, and on the conditions of the process.
To avoid damp and pre-adsorption of organic before running, or must to be reactivated.